EN 1.0345 Steel vs. EN 1.4309 Stainless Steel

Both EN 1.0345 steel and EN 1.4309 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is EN 1.4309 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
140
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
34
Fatigue Strength, MPa 170
170
Impact Strength: V-Notched Charpy, J 44
90
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 420
490
Tensile Strength: Yield (Proof), MPa 230
210

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.1
Embodied Energy, MJ/kg 19
45
Embodied Water, L/kg 48
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15
18
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
4.1
Thermal Shock Resistance, points 13
11

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.030
Chromium (Cr), % 0 to 0.3
18 to 20
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 97.2 to 99.38
64.2 to 73
Manganese (Mn), % 0.6 to 1.2
0 to 2.0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
9.0 to 12
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.35
0 to 1.5
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0