EN 1.0345 Steel vs. Grade 702C Zirconium

EN 1.0345 steel belongs to the iron alloys classification, while grade 702C zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is grade 702C zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
180
Elastic (Young's, Tensile) Modulus, GPa 190
97
Elongation at Break, % 27
13
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
36
Tensile Strength: Ultimate (UTS), MPa 420
430
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 49
22
Thermal Expansion, µm/m-K 12
5.7

Otherwise Unclassified Properties

Density, g/cm3 7.9
6.7
Embodied Water, L/kg 48
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
52
Resilience: Unit (Modulus of Resilience), kJ/m3 140
510
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15
18
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 13
55

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.1
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 97.2 to 99.38
0 to 0.3
Manganese (Mn), % 0.6 to 1.2
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0 to 0.030
Oxygen (O), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.025
0 to 0.010
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0
Zirconium (Zr), % 0
94.8 to 100