EN 1.0345 Steel vs. Reactor Grade Zirconium

EN 1.0345 steel belongs to the iron alloys classification, while reactor grade zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is reactor grade zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
98
Elongation at Break, % 27
21
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
37
Tensile Strength: Ultimate (UTS), MPa 420
330
Tensile Strength: Yield (Proof), MPa 230
160

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 49
22
Thermal Expansion, µm/m-K 12
5.9

Otherwise Unclassified Properties

Density, g/cm3 7.9
6.5
Embodied Water, L/kg 48
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
56
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130
Stiffness to Weight: Axial, points 13
8.4
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
14
Strength to Weight: Bending, points 16
16
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 13
41

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 97.2 to 99.38
0
Manganese (Mn), % 0.6 to 1.2
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0
Zirconium (Zr), % 0
99.7 to 100
Residuals, % 0
0 to 0.27