EN 1.0345 Steel vs. SAE-AISI 1211 Steel

Both EN 1.0345 steel and SAE-AISI 1211 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is SAE-AISI 1211 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
140 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
11 to 29
Fatigue Strength, MPa 170
200 to 280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 270
280 to 350
Tensile Strength: Ultimate (UTS), MPa 420
430 to 580
Tensile Strength: Yield (Proof), MPa 230
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 48
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
61 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
180 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
15 to 21
Strength to Weight: Bending, points 16
16 to 20
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 13
14 to 18

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.13
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 97.2 to 99.38
98.7 to 99.23
Manganese (Mn), % 0.6 to 1.2
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.025
0.070 to 0.12
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.010
0.1 to 0.15
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0