EN 1.0345 Steel vs. SAE-AISI H11 Steel

Both EN 1.0345 steel and SAE-AISI H11 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is SAE-AISI H11 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 420
690 to 1840

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
42
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
5.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.0
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 48
75

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15
25 to 66
Strength to Weight: Bending, points 16
22 to 43
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 13
22 to 58

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0.33 to 0.43
Chromium (Cr), % 0 to 0.3
4.8 to 5.5
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 97.2 to 99.38
89.6 to 92.5
Manganese (Mn), % 0.6 to 1.2
0.2 to 0.5
Molybdenum (Mo), % 0 to 0.080
1.1 to 1.6
Nickel (Ni), % 0 to 0.3
0 to 0.3
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0.8 to 1.2
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0.3 to 0.6