EN 1.0345 Steel vs. S28200 Stainless Steel

Both EN 1.0345 steel and S28200 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is S28200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
45
Fatigue Strength, MPa 170
430
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 270
610
Tensile Strength: Ultimate (UTS), MPa 420
870
Tensile Strength: Yield (Proof), MPa 230
460

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
900
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1330
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
18

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
12
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 19
41
Embodied Water, L/kg 48
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
330
Resilience: Unit (Modulus of Resilience), kJ/m3 140
540
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 15
32
Strength to Weight: Bending, points 16
27
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.15
Chromium (Cr), % 0 to 0.3
17 to 19
Copper (Cu), % 0 to 0.3
0.75 to 1.3
Iron (Fe), % 97.2 to 99.38
57.7 to 64.1
Manganese (Mn), % 0.6 to 1.2
17 to 19
Molybdenum (Mo), % 0 to 0.080
0.75 to 1.3
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0.4 to 0.6
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0