EN 1.0345 Steel vs. S30441 Stainless Steel

Both EN 1.0345 steel and S30441 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is S30441 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
45
Fatigue Strength, MPa 170
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 270
400
Tensile Strength: Ultimate (UTS), MPa 420
580
Tensile Strength: Yield (Proof), MPa 230
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
940
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
18
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 19
50
Embodied Water, L/kg 48
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15
21
Strength to Weight: Bending, points 16
20
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.080
Chromium (Cr), % 0 to 0.3
17.5 to 19.5
Copper (Cu), % 0 to 0.3
1.5 to 2.5
Iron (Fe), % 97.2 to 99.38
62 to 71.7
Manganese (Mn), % 0.6 to 1.2
0 to 2.0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
8.0 to 10.5
Niobium (Nb), % 0 to 0.020
0.1 to 0.5
Nitrogen (N), % 0 to 0.012
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.35
1.0 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Tungsten (W), % 0
0.2 to 0.8
Vanadium (V), % 0 to 0.020
0