EN 1.0402 Steel vs. ACI-ASTM CK35MN Steel

Both EN 1.0402 steel and ACI-ASTM CK35MN steel are iron alloys. They have 49% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0402 steel and the bottom bar is ACI-ASTM CK35MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
190
Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 24
40
Fatigue Strength, MPa 170
270
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 460
650
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
12
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
31
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.9
Embodied Energy, MJ/kg 19
81
Embodied Water, L/kg 47
210

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 94
210
Resilience: Unit (Modulus of Resilience), kJ/m3 150
240
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
22
Strength to Weight: Bending, points 17
21
Thermal Diffusivity, mm2/s 13
3.3
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0.17 to 0.24
0 to 0.035
Chromium (Cr), % 0 to 0.4
22 to 24
Copper (Cu), % 0
0 to 0.4
Iron (Fe), % 97.7 to 99.43
43.4 to 51.8
Manganese (Mn), % 0.4 to 0.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
6.0 to 6.8
Nickel (Ni), % 0 to 0.4
20 to 22
Nitrogen (N), % 0
0.21 to 0.32
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.020