EN 1.0451 Steel vs. 6262 Aluminum

EN 1.0451 steel belongs to the iron alloys classification, while 6262 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is 6262 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
68
Elongation at Break, % 27
4.6 to 10
Fatigue Strength, MPa 180
90 to 110
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Shear Strength, MPa 270
170 to 240
Tensile Strength: Ultimate (UTS), MPa 420
290 to 390
Tensile Strength: Yield (Proof), MPa 240
270 to 360

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 400
160
Melting Completion (Liquidus), °C 1460
650
Melting Onset (Solidus), °C 1420
580
Specific Heat Capacity, J/kg-K 470
890
Thermal Conductivity, W/m-K 49
170
Thermal Expansion, µm/m-K 12
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
44
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
140

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
10
Density, g/cm3 7.9
2.8
Embodied Carbon, kg CO2/kg material 1.5
8.3
Embodied Energy, MJ/kg 19
150
Embodied Water, L/kg 48
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
17 to 31
Resilience: Unit (Modulus of Resilience), kJ/m3 150
530 to 940
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
48
Strength to Weight: Axial, points 15
29 to 39
Strength to Weight: Bending, points 16
35 to 42
Thermal Diffusivity, mm2/s 13
69
Thermal Shock Resistance, points 13
13 to 18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.060
94.7 to 97.8
Bismuth (Bi), % 0
0.4 to 0.7
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 0 to 0.3
0.040 to 0.14
Copper (Cu), % 0 to 0.3
0.15 to 0.4
Iron (Fe), % 97.2 to 99.58
0 to 0.7
Lead (Pb), % 0
0.4 to 0.7
Magnesium (Mg), % 0
0.8 to 1.2
Manganese (Mn), % 0.4 to 1.2
0 to 0.15
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.35
0.4 to 0.8
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0 to 0.040
0 to 0.15
Vanadium (V), % 0 to 0.020
0
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.15