EN 1.0451 Steel vs. EN 1.1104 Steel

Both EN 1.0451 steel and EN 1.1104 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is EN 1.1104 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
27
Fatigue Strength, MPa 180
210
Impact Strength: V-Notched Charpy, J 62
88
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 270
280
Tensile Strength: Ultimate (UTS), MPa 420
440
Tensile Strength: Yield (Proof), MPa 240
280

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
49
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 48
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
100
Resilience: Unit (Modulus of Resilience), kJ/m3 150
200
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
15
Strength to Weight: Bending, points 16
16
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 13
14

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0.020 to 0.024
Carbon (C), % 0 to 0.15
0 to 0.16
Chromium (Cr), % 0 to 0.3
0 to 0.3
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 97.2 to 99.58
96.6 to 99.38
Manganese (Mn), % 0.4 to 1.2
0.6 to 1.5
Molybdenum (Mo), % 0 to 0.080
0 to 0.080
Nickel (Ni), % 0 to 0.3
0 to 0.5
Niobium (Nb), % 0 to 0.010
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.0050
Titanium (Ti), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0 to 0.020
0 to 0.050