EN 1.0451 Steel vs. Grade CX2MW Nickel

EN 1.0451 steel belongs to the iron alloys classification, while grade CX2MW nickel belongs to the nickel alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is grade CX2MW nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 27
34
Fatigue Strength, MPa 180
260
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
84
Tensile Strength: Ultimate (UTS), MPa 420
620
Tensile Strength: Yield (Proof), MPa 240
350

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1550
Melting Onset (Solidus), °C 1420
1490
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 49
10
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
65
Density, g/cm3 7.9
8.9
Embodied Carbon, kg CO2/kg material 1.5
12
Embodied Energy, MJ/kg 19
170
Embodied Water, L/kg 48
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
180
Resilience: Unit (Modulus of Resilience), kJ/m3 150
290
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15
19
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
2.7
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.15
0 to 0.020
Chromium (Cr), % 0 to 0.3
20 to 22.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 97.2 to 99.58
2.0 to 6.0
Manganese (Mn), % 0.4 to 1.2
0 to 1.0
Molybdenum (Mo), % 0 to 0.080
12.5 to 14.5
Nickel (Ni), % 0 to 0.3
51.3 to 63
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.8
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0 to 0.040
0
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0 to 0.020
0 to 0.35