EN 1.0451 Steel vs. Nickel 890

EN 1.0451 steel belongs to the iron alloys classification, while nickel 890 belongs to the nickel alloys. They have a modest 27% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is nickel 890.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
39
Fatigue Strength, MPa 180
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 270
400
Tensile Strength: Ultimate (UTS), MPa 420
590
Tensile Strength: Yield (Proof), MPa 240
230

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
47
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 1.5
8.2
Embodied Energy, MJ/kg 19
120
Embodied Water, L/kg 48
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
180
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
20
Strength to Weight: Bending, points 16
19
Thermal Shock Resistance, points 13
15

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0.050 to 0.6
Carbon (C), % 0 to 0.15
0.060 to 0.14
Chromium (Cr), % 0 to 0.3
23.5 to 28.5
Copper (Cu), % 0 to 0.3
0 to 0.75
Iron (Fe), % 97.2 to 99.58
17.3 to 33.9
Manganese (Mn), % 0.4 to 1.2
0 to 1.5
Molybdenum (Mo), % 0 to 0.080
1.0 to 2.0
Nickel (Ni), % 0 to 0.3
40 to 45
Niobium (Nb), % 0 to 0.010
0.2 to 1.0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.35
1.0 to 2.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Tantalum (Ta), % 0
0.1 to 0.6
Titanium (Ti), % 0 to 0.040
0.15 to 0.6
Vanadium (V), % 0 to 0.020
0