EN 1.0451 Steel vs. SAE-AISI M30 Steel

Both EN 1.0451 steel and SAE-AISI M30 steel are iron alloys. They have 79% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is SAE-AISI M30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
78
Tensile Strength: Ultimate (UTS), MPa 420
800 to 2170

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1550
Melting Onset (Solidus), °C 1420
1500
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 49
24
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
26
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 1.5
7.2
Embodied Energy, MJ/kg 19
100
Embodied Water, L/kg 48
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
27 to 74
Strength to Weight: Bending, points 16
24 to 46
Thermal Diffusivity, mm2/s 13
6.6
Thermal Shock Resistance, points 13
25 to 67

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.15
0.75 to 0.85
Chromium (Cr), % 0 to 0.3
3.5 to 4.3
Cobalt (Co), % 0
4.5 to 5.5
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 97.2 to 99.58
75.2 to 80.9
Manganese (Mn), % 0.4 to 1.2
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.080
7.8 to 9.0
Nickel (Ni), % 0 to 0.3
0 to 0.3
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0.2 to 0.45
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.040
0
Tungsten (W), % 0
1.3 to 2.3
Vanadium (V), % 0 to 0.020
1.0 to 1.4