EN 1.0451 Steel vs. N06255 Nickel

EN 1.0451 steel belongs to the iron alloys classification, while N06255 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is N06255 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 27
45
Fatigue Strength, MPa 180
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
81
Shear Strength, MPa 270
460
Tensile Strength: Ultimate (UTS), MPa 420
660
Tensile Strength: Yield (Proof), MPa 240
250

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
55
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 1.5
9.4
Embodied Energy, MJ/kg 19
130
Embodied Water, L/kg 48
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
230
Resilience: Unit (Modulus of Resilience), kJ/m3 150
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15
22
Strength to Weight: Bending, points 16
20
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 0 to 0.3
23 to 26
Copper (Cu), % 0 to 0.3
0 to 1.2
Iron (Fe), % 97.2 to 99.58
6.0 to 24
Manganese (Mn), % 0.4 to 1.2
0 to 1.0
Molybdenum (Mo), % 0 to 0.080
6.0 to 9.0
Nickel (Ni), % 0 to 0.3
47 to 52
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.040
0 to 0.69
Tungsten (W), % 0
0 to 3.0
Vanadium (V), % 0 to 0.020
0