EN 1.0451 Steel vs. S44536 Stainless Steel

Both EN 1.0451 steel and S44536 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is S44536 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
22
Fatigue Strength, MPa 180
190
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 270
290
Tensile Strength: Ultimate (UTS), MPa 420
460
Tensile Strength: Yield (Proof), MPa 240
280

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
990
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
21
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.5
2.8
Embodied Energy, MJ/kg 19
41
Embodied Water, L/kg 48
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
89
Resilience: Unit (Modulus of Resilience), kJ/m3 150
200
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 15
17
Strength to Weight: Bending, points 16
17
Thermal Diffusivity, mm2/s 13
5.6
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.15
0 to 0.015
Chromium (Cr), % 0 to 0.3
20 to 23
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 97.2 to 99.58
72.8 to 80
Manganese (Mn), % 0.4 to 1.2
0 to 1.0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0 to 0.5
Niobium (Nb), % 0 to 0.010
0.050 to 0.8
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.040
0 to 0.8
Vanadium (V), % 0 to 0.020
0