EN 1.0455 Cast Steel vs. EN 1.4469 Stainless Steel

Both EN 1.0455 cast steel and EN 1.4469 stainless steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0455 cast steel and the bottom bar is EN 1.4469 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 25
25
Fatigue Strength, MPa 200
380
Impact Strength: V-Notched Charpy, J 35
56
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
81
Tensile Strength: Ultimate (UTS), MPa 530
740
Tensile Strength: Yield (Proof), MPa 270
550

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
17
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
21
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.1
Embodied Energy, MJ/kg 18
57
Embodied Water, L/kg 46
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
170
Resilience: Unit (Modulus of Resilience), kJ/m3 190
730
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 18
23
Thermal Diffusivity, mm2/s 14
4.6
Thermal Shock Resistance, points 17
20

Alloy Composition

Carbon (C), % 0 to 0.23
0 to 0.030
Chromium (Cr), % 0
25 to 27
Copper (Cu), % 0
0 to 1.3
Iron (Fe), % 97.9 to 100
56.4 to 65.9
Manganese (Mn), % 0 to 1.2
0 to 1.0
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 0
6.0 to 8.0
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.025