EN 1.0473 Steel vs. EN 1.5680 Steel

Both EN 1.0473 steel and EN 1.5680 steel are iron alloys. They have a very high 95% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.0473 steel and the bottom bar is EN 1.5680 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
23
Fatigue Strength, MPa 250
310
Impact Strength: V-Notched Charpy, J 46
71
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 360
390
Tensile Strength: Ultimate (UTS), MPa 570
620
Tensile Strength: Yield (Proof), MPa 360
440

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
48
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.9
Embodied Energy, MJ/kg 20
26
Embodied Water, L/kg 49
55

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
130
Resilience: Unit (Modulus of Resilience), kJ/m3 340
510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 18
18

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0.1 to 0.22
0 to 0.15
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.3 to 98.8
93.4 to 95
Manganese (Mn), % 1.1 to 1.7
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
4.8 to 5.3
Niobium (Nb), % 0 to 0.040
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.6
0 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.0050
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0 to 0.050