EN 1.0501 Steel vs. AISI 202 Stainless Steel

Both EN 1.0501 steel and AISI 202 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0501 steel and the bottom bar is AISI 202 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
210 to 300
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
14 to 45
Fatigue Strength, MPa 190
290 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 350
490 to 590
Tensile Strength: Ultimate (UTS), MPa 560
700 to 980
Tensile Strength: Yield (Proof), MPa 280
310 to 580

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
910
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 19
40
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 210
250 to 840
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
25 to 35
Strength to Weight: Bending, points 19
23 to 29
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 18
15 to 21

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.15
Chromium (Cr), % 0 to 0.4
17 to 19
Iron (Fe), % 97.4 to 99.18
63.5 to 71.5
Manganese (Mn), % 0.5 to 0.8
7.5 to 10
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
4.0 to 6.0
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.045
0 to 0.060
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030