EN 1.0501 (C35) Non-Alloy Steel

EN 1.0501 steel is a carbon (non-alloy) steel formulated for primary forming into wrought products. Cited properties are appropriate for the normalized condition. 1.0501 is the EN numeric designation for this material. C35 is the EN chemical designation.

It has a moderately low thermal conductivity among the wrought carbon or non-alloy steels in the database.

The graph bars on the material properties cards below compare EN 1.0501 steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

160

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

19 %

Fatigue Strength

190 MPa 28 x 103 psi

Impact Strength: V-Notched Charpy

23 J 17 ft-lb

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

350 MPa 51 x 103 psi

Tensile Strength: Ultimate (UTS)

560 MPa 81 x 103 psi

Tensile Strength: Yield (Proof)

280 MPa 41 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

48 W/m-K 28 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.3 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.1 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.2 x 103 BTU/lb

Embodied Water

47 L/kg 5.6 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

90 MJ/m3

Resilience: Unit (Modulus of Resilience)

210 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

20 points

Strength to Weight: Bending

19 points

Thermal Diffusivity

13 mm2/s

Thermal Shock Resistance

18 points

Alloy Composition

Iron (Fe)Fe 97.4 to 99.18
Manganese (Mn)Mn 0.5 to 0.8
Carbon (C)C 0.32 to 0.39
Silicon (Si)Si 0 to 0.4
Chromium (Cr)Cr 0 to 0.4
Nickel (Ni)Ni 0 to 0.4
Molybdenum (Mo)Mo 0 to 0.1
Phosphorus (P)P 0 to 0.045
Sulfur (S)S 0 to 0.045

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10250-2: Open die steel forgings for general engineering purposes - Part 2: Non-alloy quality and special steels

Carbon Steel Handbook, D. Gandy, 2007

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015