EN 1.0501 Steel vs. EN 1.4462 Stainless Steel

Both EN 1.0501 steel and EN 1.4462 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0501 steel and the bottom bar is EN 1.4462 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
240
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
26
Fatigue Strength, MPa 190
370
Impact Strength: V-Notched Charpy, J 23
90
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 350
500
Tensile Strength: Ultimate (UTS), MPa 560
780
Tensile Strength: Yield (Proof), MPa 280
520

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1060
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.6
Embodied Energy, MJ/kg 19
49
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
180
Resilience: Unit (Modulus of Resilience), kJ/m3 210
670
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
28
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 18
21

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.030
Chromium (Cr), % 0 to 0.4
21 to 23
Iron (Fe), % 97.4 to 99.18
63.7 to 71.9
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
2.5 to 3.5
Nickel (Ni), % 0 to 0.4
4.5 to 6.5
Nitrogen (N), % 0
0.1 to 0.22
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.015