EN 1.0501 Steel vs. EN 1.6932 Steel

Both EN 1.0501 steel and EN 1.6932 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0501 steel and the bottom bar is EN 1.6932 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
270
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
14
Fatigue Strength, MPa 190
460
Impact Strength: V-Notched Charpy, J 23
40
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
540
Tensile Strength: Ultimate (UTS), MPa 560
900
Tensile Strength: Yield (Proof), MPa 280
720

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
45
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
4.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 19
27
Embodied Water, L/kg 47
56

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
1370
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
32
Strength to Weight: Bending, points 19
26
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 18
26

Alloy Composition

Carbon (C), % 0.32 to 0.39
0.24 to 0.32
Chromium (Cr), % 0 to 0.4
1.0 to 1.5
Iron (Fe), % 97.4 to 99.18
94.5 to 96.4
Manganese (Mn), % 0.5 to 0.8
0.15 to 0.4
Molybdenum (Mo), % 0 to 0.1
0.35 to 0.55
Nickel (Ni), % 0 to 0.4
1.8 to 2.1
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.045
0 to 0.035
Vanadium (V), % 0
0.050 to 0.15