EN 1.0501 Steel vs. S32101 Stainless Steel

Both EN 1.0501 steel and S32101 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0501 steel and the bottom bar is S32101 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
34
Fatigue Strength, MPa 190
400
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 350
490
Tensile Strength: Ultimate (UTS), MPa 560
740
Tensile Strength: Yield (Proof), MPa 280
500

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
15
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 19
38
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
230
Resilience: Unit (Modulus of Resilience), kJ/m3 210
640
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 18
20

Alloy Composition

Carbon (C), % 0.32 to 0.39
0 to 0.040
Chromium (Cr), % 0 to 0.4
21 to 22
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 97.4 to 99.18
67.3 to 73.3
Manganese (Mn), % 0.5 to 0.8
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.1
0.1 to 0.8
Nickel (Ni), % 0 to 0.4
1.4 to 1.7
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030