MakeItFrom.com
Menu (ESC)

EN 1.0511 Steel vs. ACI-ASTM CF16F Steel

Both EN 1.0511 steel and ACI-ASTM CF16F steel are iron alloys. They have 68% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0511 steel and the bottom bar is ACI-ASTM CF16F steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
50
Fatigue Strength, MPa 200
270
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 590
530
Tensile Strength: Yield (Proof), MPa 300
280

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
16
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 19
47
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
220
Resilience: Unit (Modulus of Resilience), kJ/m3 230
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 13
4.3
Thermal Shock Resistance, points 19
12

Alloy Composition

Carbon (C), % 0.37 to 0.44
0 to 0.16
Chromium (Cr), % 0 to 0.4
18 to 21
Iron (Fe), % 97.4 to 99.13
61.3 to 72.8
Manganese (Mn), % 0.5 to 0.8
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
0 to 1.5
Nickel (Ni), % 0 to 0.4
9.0 to 12
Phosphorus (P), % 0 to 0.045
0 to 0.17
Selenium (Se), % 0
0.2 to 0.35
Silicon (Si), % 0 to 0.4
0 to 2.0
Sulfur (S), % 0 to 0.045
0 to 0.040