MakeItFrom.com
Menu (ESC)

EN 1.0511 Steel vs. N08020 Stainless Steel

Both EN 1.0511 steel and N08020 stainless steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0511 steel and the bottom bar is N08020 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
15 to 34
Fatigue Strength, MPa 200
210 to 240
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 370
380 to 410
Tensile Strength: Ultimate (UTS), MPa 590
610 to 620
Tensile Strength: Yield (Proof), MPa 300
270 to 420

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 48
12
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
38
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.4
6.6
Embodied Energy, MJ/kg 19
92
Embodied Water, L/kg 47
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 84
83 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 230
180 to 440
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 13
3.2
Thermal Shock Resistance, points 19
15

Alloy Composition

Carbon (C), % 0.37 to 0.44
0 to 0.070
Chromium (Cr), % 0 to 0.4
19 to 21
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 97.4 to 99.13
29.9 to 44
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
2.0 to 3.0
Nickel (Ni), % 0 to 0.4
32 to 38
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.035