EN 1.0528 Steel vs. AWS E16-8-2

Both EN 1.0528 steel and AWS E16-8-2 are iron alloys. They have 74% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0528 steel and the bottom bar is AWS E16-8-2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
40
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 520
620

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
16
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
15
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.2
Embodied Energy, MJ/kg 19
45
Embodied Water, L/kg 47
140

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 13
4.2
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0.27 to 0.34
0 to 0.1
Chromium (Cr), % 0 to 0.4
14.5 to 16.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 97.5 to 99.23
68 to 76.5
Manganese (Mn), % 0.5 to 0.8
0.5 to 2.5
Molybdenum (Mo), % 0 to 0.1
1.0 to 2.0
Nickel (Ni), % 0 to 0.4
7.5 to 9.5
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.045
0 to 0.030