EN 1.0528 Steel vs. EN 1.0477 Steel

Both EN 1.0528 steel and EN 1.0477 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0528 steel and the bottom bar is EN 1.0477 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
24
Fatigue Strength, MPa 180
170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320
280
Tensile Strength: Ultimate (UTS), MPa 520
440
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
49
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88
90
Resilience: Unit (Modulus of Resilience), kJ/m3 180
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
16
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 16
14

Alloy Composition

Aluminum (Al), % 0
0 to 0.060
Carbon (C), % 0.27 to 0.34
0 to 0.18
Chromium (Cr), % 0 to 0.4
0 to 0.3
Copper (Cu), % 0
0 to 0.2
Iron (Fe), % 97.5 to 99.23
96.9 to 99.4
Manganese (Mn), % 0.5 to 0.8
0.6 to 1.4
Molybdenum (Mo), % 0 to 0.1
0 to 0.080
Nickel (Ni), % 0 to 0.4
0 to 0.3
Niobium (Nb), % 0
0 to 0.030
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.045
0 to 0.015
Vanadium (V), % 0
0 to 0.050