EN 1.0528 Steel vs. SAE-AISI 4626 Steel

Both EN 1.0528 steel and SAE-AISI 4626 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0528 steel and the bottom bar is SAE-AISI 4626 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
25
Fatigue Strength, MPa 180
240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 320
320
Tensile Strength: Ultimate (UTS), MPa 520
500
Tensile Strength: Yield (Proof), MPa 260
330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
44
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 88
110
Resilience: Unit (Modulus of Resilience), kJ/m3 180
290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18
18
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 16
15

Alloy Composition

Carbon (C), % 0.27 to 0.34
0.24 to 0.29
Chromium (Cr), % 0 to 0.4
0
Iron (Fe), % 97.5 to 99.23
97.4 to 98.3
Manganese (Mn), % 0.5 to 0.8
0.45 to 0.65
Molybdenum (Mo), % 0 to 0.1
0.15 to 0.25
Nickel (Ni), % 0 to 0.4
0.7 to 1.0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.040