EN 1.0558 Cast Steel vs. ACI-ASTM CA40 Steel

Both EN 1.0558 cast steel and ACI-ASTM CA40 steel are iron alloys. They have 85% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is ACI-ASTM CA40 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
10
Fatigue Strength, MPa 230
460
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 640
910
Tensile Strength: Yield (Proof), MPa 340
860

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
750
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1500
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
25
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
7.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.0
Embodied Energy, MJ/kg 18
28
Embodied Water, L/kg 45
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
89
Resilience: Unit (Modulus of Resilience), kJ/m3 300
1910
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
33
Strength to Weight: Bending, points 21
27
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 20
33

Alloy Composition

Carbon (C), % 0
0.2 to 0.4
Chromium (Cr), % 0
11.5 to 14
Iron (Fe), % 99.935 to 100
81.5 to 88.3
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.040