EN 1.0558 Cast Steel vs. ACI-ASTM CF10SMnN Steel

Both EN 1.0558 cast steel and ACI-ASTM CF10SMnN steel are iron alloys. They have 62% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is ACI-ASTM CF10SMnN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
34
Fatigue Strength, MPa 230
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 640
660
Tensile Strength: Yield (Proof), MPa 340
330

Thermal Properties

Latent Heat of Fusion, J/g 250
340
Maximum Temperature: Mechanical, °C 400
900
Melting Completion (Liquidus), °C 1470
1360
Melting Onset (Solidus), °C 1430
1310
Specific Heat Capacity, J/kg-K 470
500
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
15
Density, g/cm3 7.9
7.5
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 18
45
Embodied Water, L/kg 45
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
180
Resilience: Unit (Modulus of Resilience), kJ/m3 300
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 21
22
Thermal Shock Resistance, points 20
15

Alloy Composition

Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
16 to 18
Iron (Fe), % 99.935 to 100
59.1 to 65.4
Manganese (Mn), % 0
7.0 to 9.0
Nickel (Ni), % 0
8.0 to 9.0
Nitrogen (N), % 0
0.080 to 0.18
Phosphorus (P), % 0 to 0.035
0 to 0.060
Silicon (Si), % 0
3.5 to 4.5
Sulfur (S), % 0 to 0.030
0 to 0.030