EN 1.0558 Cast Steel vs. AISI 316LN Stainless Steel

Both EN 1.0558 cast steel and AISI 316LN stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is AISI 316LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
42
Fatigue Strength, MPa 230
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 640
590
Tensile Strength: Yield (Proof), MPa 340
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
940
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
3.8
Embodied Energy, MJ/kg 18
53
Embodied Water, L/kg 45
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
200
Resilience: Unit (Modulus of Resilience), kJ/m3 300
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 20
13

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
16 to 18
Iron (Fe), % 99.935 to 100
62 to 71.9
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
10 to 14
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030