EN 1.0558 Cast Steel vs. AWS E320LR

Both EN 1.0558 cast steel and AWS E320LR are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is AWS E320LR.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 640
580

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1470
1410
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
36
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 1.4
6.2
Embodied Energy, MJ/kg 18
87
Embodied Water, L/kg 45
220

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Shock Resistance, points 20
15

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
19 to 21
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 99.935 to 100
32.7 to 42.5
Manganese (Mn), % 0
1.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
32 to 36
Niobium (Nb), % 0
0 to 0.4
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.015