EN 1.0558 Cast Steel vs. EN 1.4306 Stainless Steel

Both EN 1.0558 cast steel and EN 1.4306 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is EN 1.4306 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
14 to 45
Fatigue Strength, MPa 230
190 to 330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 640
580 to 900
Tensile Strength: Yield (Proof), MPa 340
210 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
960
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.2
Embodied Energy, MJ/kg 18
45
Embodied Water, L/kg 45
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
110 to 200
Resilience: Unit (Modulus of Resilience), kJ/m3 300
110 to 820
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
21 to 32
Strength to Weight: Bending, points 21
20 to 27
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 20
13 to 20

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
18 to 20
Iron (Fe), % 99.935 to 100
64.8 to 72
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015