EN 1.0558 Cast Steel vs. EN 1.7707 Steel

Both EN 1.0558 cast steel and EN 1.7707 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is EN 1.7707 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
11
Fatigue Strength, MPa 230
500
Impact Strength: V-Notched Charpy, J 33
31
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 640
1010
Tensile Strength: Yield (Proof), MPa 340
800

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
460
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
3.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 18
27
Embodied Water, L/kg 45
58

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
110
Resilience: Unit (Modulus of Resilience), kJ/m3 300
1690
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
36
Strength to Weight: Bending, points 21
29
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 20
29

Alloy Composition

Carbon (C), % 0
0.26 to 0.34
Chromium (Cr), % 0
2.3 to 2.7
Iron (Fe), % 99.935 to 100
94.7 to 96.8
Manganese (Mn), % 0
0.4 to 0.7
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0
0 to 0.6
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035
Vanadium (V), % 0
0.1 to 0.2