EN 1.0558 Cast Steel vs. EN 2.4889 Nickel

EN 1.0558 cast steel belongs to the iron alloys classification, while EN 2.4889 nickel belongs to the nickel alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is EN 2.4889 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
39
Fatigue Strength, MPa 230
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 640
720
Tensile Strength: Yield (Proof), MPa 340
270

Thermal Properties

Latent Heat of Fusion, J/g 250
350
Maximum Temperature: Mechanical, °C 400
1200
Melting Completion (Liquidus), °C 1470
1350
Melting Onset (Solidus), °C 1430
1300
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
13
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
42
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 1.4
6.9
Embodied Energy, MJ/kg 18
98
Embodied Water, L/kg 45
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
220
Resilience: Unit (Modulus of Resilience), kJ/m3 300
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
25
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 14
3.4
Thermal Shock Resistance, points 20
19

Alloy Composition

Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.090
Chromium (Cr), % 0
26 to 29
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 99.935 to 100
21 to 25
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0
45 to 50.4
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0
2.5 to 3.0
Sulfur (S), % 0 to 0.030
0 to 0.010