EN 1.0558 Cast Steel vs. Grade FDCrV Steel

Both EN 1.0558 cast steel and grade FDCrV steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is grade FDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 640
1800

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
48
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 18
26
Embodied Water, L/kg 45
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
64
Strength to Weight: Bending, points 21
42
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 20
53

Alloy Composition

Carbon (C), % 0
0.62 to 0.72
Chromium (Cr), % 0
0.4 to 0.6
Copper (Cu), % 0
0 to 0.12
Iron (Fe), % 99.935 to 100
97.8 to 98.8
Manganese (Mn), % 0
0.5 to 0.9
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0
0.15 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0.15 to 0.25