EN 1.0558 Cast Steel vs. N07773 Nickel

EN 1.0558 cast steel belongs to the iron alloys classification, while N07773 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is N07773 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
40
Fatigue Strength, MPa 230
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 640
710
Tensile Strength: Yield (Proof), MPa 340
270

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
990
Melting Completion (Liquidus), °C 1470
1510
Melting Onset (Solidus), °C 1430
1460
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
75
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 1.4
13
Embodied Energy, MJ/kg 18
180
Embodied Water, L/kg 45
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
220
Resilience: Unit (Modulus of Resilience), kJ/m3 300
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 22
23
Strength to Weight: Bending, points 21
21
Thermal Shock Resistance, points 20
20

Alloy Composition

Aluminum (Al), % 0
0 to 2.0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
18 to 27
Iron (Fe), % 99.935 to 100
0 to 32
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 5.5
Nickel (Ni), % 0
45 to 60
Niobium (Nb), % 0
2.5 to 6.0
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 2.0
Tungsten (W), % 0
0 to 6.0