EN 1.0558 Cast Steel vs. S32950 Stainless Steel

Both EN 1.0558 cast steel and S32950 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is S32950 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
17
Fatigue Strength, MPa 230
330
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 640
780
Tensile Strength: Yield (Proof), MPa 340
550

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
17
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.4
Embodied Energy, MJ/kg 18
47
Embodied Water, L/kg 45
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
120
Resilience: Unit (Modulus of Resilience), kJ/m3 300
730
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
28
Strength to Weight: Bending, points 21
24
Thermal Diffusivity, mm2/s 14
4.3
Thermal Shock Resistance, points 20
21

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
26 to 29
Iron (Fe), % 99.935 to 100
60.3 to 69.4
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
1.0 to 2.5
Nickel (Ni), % 0
3.5 to 5.2
Nitrogen (N), % 0
0.15 to 0.35
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.010