EN 1.0565 Steel vs. AWS ER80S-B6

Both EN 1.0565 steel and AWS ER80S-B6 are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0565 steel and the bottom bar is AWS ER80S-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 550
620
Tensile Strength: Yield (Proof), MPa 360
540

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
4.7
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.8
Embodied Energy, MJ/kg 22
24
Embodied Water, L/kg 49
71

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 340
750
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
22
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 17
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.1
Chromium (Cr), % 0 to 0.3
4.5 to 6.0
Copper (Cu), % 0 to 0.3
0 to 0.35
Iron (Fe), % 96.2 to 99
90.6 to 94.7
Manganese (Mn), % 0.9 to 1.7
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.080
0.45 to 0.65
Nickel (Ni), % 0 to 0.5
0 to 0.6
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.5