EN 1.0565 Steel vs. SAE-AISI 1140 Steel

Both EN 1.0565 steel and SAE-AISI 1140 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0565 steel and the bottom bar is SAE-AISI 1140 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24
14 to 18
Fatigue Strength, MPa 260
230 to 370
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 350
370 to 420
Tensile Strength: Ultimate (UTS), MPa 550
600 to 700
Tensile Strength: Yield (Proof), MPa 360
340 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 22
18
Embodied Water, L/kg 49
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
89 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 340
310 to 870
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
21 to 25
Strength to Weight: Bending, points 19
20 to 22
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
18 to 21

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0.37 to 0.44
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.2 to 99
98.4 to 98.9
Manganese (Mn), % 0.9 to 1.7
0.7 to 1.0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.015
0.080 to 0.13
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0