EN 1.0565 Steel vs. S33425 Stainless Steel

Both EN 1.0565 steel and S33425 stainless steel are iron alloys. They have 53% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0565 steel and the bottom bar is S33425 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 24
45
Fatigue Strength, MPa 260
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 350
400
Tensile Strength: Ultimate (UTS), MPa 550
580
Tensile Strength: Yield (Proof), MPa 360
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
27
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
5.1
Embodied Energy, MJ/kg 22
71
Embodied Water, L/kg 49
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
210
Resilience: Unit (Modulus of Resilience), kJ/m3 340
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 17
13

Alloy Composition

Aluminum (Al), % 0 to 0.060
0.15 to 0.6
Carbon (C), % 0 to 0.2
0 to 0.080
Chromium (Cr), % 0 to 0.3
21 to 23
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.2 to 99
47.2 to 56.7
Manganese (Mn), % 0.9 to 1.7
0 to 1.5
Molybdenum (Mo), % 0 to 0.080
2.0 to 3.0
Nickel (Ni), % 0 to 0.5
20 to 23
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0 to 0.030
0.15 to 0.6
Vanadium (V), % 0 to 0.1
0