EN 1.0565 Steel vs. S44535 Stainless Steel

Both EN 1.0565 steel and S44535 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0565 steel and the bottom bar is S44535 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 24
28
Fatigue Strength, MPa 260
210
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 350
290
Tensile Strength: Ultimate (UTS), MPa 550
450
Tensile Strength: Yield (Proof), MPa 360
290

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
21
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
11
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.4
Embodied Energy, MJ/kg 22
34
Embodied Water, L/kg 49
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 340
200
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 14
5.6
Thermal Shock Resistance, points 17
15

Alloy Composition

Aluminum (Al), % 0 to 0.060
0 to 0.5
Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 0 to 0.3
20 to 24
Copper (Cu), % 0 to 0.3
0 to 0.5
Iron (Fe), % 96.2 to 99
73.2 to 79.6
Lanthanum (La), % 0
0.040 to 0.2
Manganese (Mn), % 0.9 to 1.7
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.050
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0 to 0.030
0.030 to 0.2
Vanadium (V), % 0 to 0.1
0