EN 1.0566 Steel vs. 5056 Aluminum

EN 1.0566 steel belongs to the iron alloys classification, while 5056 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0566 steel and the bottom bar is 5056 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
67
Elongation at Break, % 24
4.9 to 31
Fatigue Strength, MPa 270
140 to 200
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
25
Shear Strength, MPa 350
170 to 240
Tensile Strength: Ultimate (UTS), MPa 550
290 to 460
Tensile Strength: Yield (Proof), MPa 370
150 to 410

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 400
190
Melting Completion (Liquidus), °C 1460
640
Melting Onset (Solidus), °C 1420
570
Specific Heat Capacity, J/kg-K 470
910
Thermal Conductivity, W/m-K 50
130
Thermal Expansion, µm/m-K 12
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
29
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
99

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
9.5
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.6
9.0
Embodied Energy, MJ/kg 22
150
Embodied Water, L/kg 50
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
12 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 360
170 to 1220
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 19
30 to 48
Strength to Weight: Bending, points 19
36 to 50
Thermal Diffusivity, mm2/s 14
53
Thermal Shock Resistance, points 17
13 to 20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
93 to 95.4
Carbon (C), % 0 to 0.18
0
Chromium (Cr), % 0 to 0.3
0.050 to 0.2
Copper (Cu), % 0 to 0.3
0 to 0.1
Iron (Fe), % 96.2 to 98.9
0 to 0.4
Magnesium (Mg), % 0
4.5 to 5.6
Manganese (Mn), % 1.1 to 1.7
0.050 to 0.2
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.5
0 to 0.3
Sulfur (S), % 0 to 0.0080
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15