EN 1.0571 Steel vs. A356.0 Aluminum

EN 1.0571 steel belongs to the iron alloys classification, while A356.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is A356.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
70
Elongation at Break, % 23
3.0 to 6.0
Fatigue Strength, MPa 220
50 to 90
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Tensile Strength: Ultimate (UTS), MPa 550
160 to 270
Tensile Strength: Yield (Proof), MPa 310
83 to 200

Thermal Properties

Latent Heat of Fusion, J/g 250
500
Maximum Temperature: Mechanical, °C 400
170
Melting Completion (Liquidus), °C 1460
610
Melting Onset (Solidus), °C 1420
570
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 52
150
Thermal Expansion, µm/m-K 12
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
40
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
140

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
9.5
Density, g/cm3 7.8
2.6
Embodied Carbon, kg CO2/kg material 1.6
8.0
Embodied Energy, MJ/kg 21
150
Embodied Water, L/kg 49
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
4.8 to 15
Resilience: Unit (Modulus of Resilience), kJ/m3 260
49 to 300
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
53
Strength to Weight: Axial, points 19
17 to 29
Strength to Weight: Bending, points 19
25 to 36
Thermal Diffusivity, mm2/s 14
64
Thermal Shock Resistance, points 17
7.6 to 13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.060
91.1 to 93.3
Carbon (C), % 0 to 0.2
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.2
0 to 0.2
Iron (Fe), % 96.5 to 99
0 to 0.2
Magnesium (Mg), % 0
0.25 to 0.45
Manganese (Mn), % 0.9 to 1.7
0 to 0.1
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.1 to 0.5
6.5 to 7.5
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.2
Vanadium (V), % 0 to 0.1
0
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15