EN 1.0571 Steel vs. AISI 312 Stainless Steel

Both EN 1.0571 steel and AISI 312 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is AISI 312 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
28
Fatigue Strength, MPa 220
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Shear Strength, MPa 350
510
Tensile Strength: Ultimate (UTS), MPa 550
780
Tensile Strength: Yield (Proof), MPa 310
510

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
16
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
48
Embodied Water, L/kg 49
170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
190
Resilience: Unit (Modulus of Resilience), kJ/m3 260
640
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
28
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 14
4.3
Thermal Shock Resistance, points 17
21

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 0 to 0.3
24 to 26
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 96.5 to 99
62.2 to 69.2
Manganese (Mn), % 0.9 to 1.7
0 to 2.0
Molybdenum (Mo), % 0 to 0.080
1.2 to 2.0
Nickel (Ni), % 0 to 0.3
5.5 to 6.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0.14 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0.1 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0 to 0.1
0