EN 1.0571 Steel vs. ASTM A204 Steel

Both EN 1.0571 steel and ASTM A204 steel are iron alloys.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
18 to 22
Fatigue Strength, MPa 220
200 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
330 to 360
Tensile Strength: Ultimate (UTS), MPa 550
520 to 590
Tensile Strength: Yield (Proof), MPa 310
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420 to 1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
52
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
20
Embodied Water, L/kg 49
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 260
220 to 290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
18 to 21
Strength to Weight: Bending, points 19
18 to 20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
15 to 17