EN 1.0571 Steel vs. EN 1.4557 Stainless Steel

Both EN 1.0571 steel and EN 1.4557 stainless steel are iron alloys. They have 54% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is EN 1.4557 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
40
Fatigue Strength, MPa 220
260
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 550
560
Tensile Strength: Yield (Proof), MPa 310
300

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1090
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 52
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
29
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.6
5.6
Embodied Energy, MJ/kg 21
76
Embodied Water, L/kg 49
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
190
Resilience: Unit (Modulus of Resilience), kJ/m3 260
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 17
12

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.020
Chromium (Cr), % 0 to 0.3
19.5 to 20.5
Copper (Cu), % 0 to 0.2
0.5 to 1.0
Iron (Fe), % 96.5 to 99
49.5 to 56.3
Manganese (Mn), % 0.9 to 1.7
0 to 1.2
Molybdenum (Mo), % 0 to 0.080
6.0 to 7.0
Nickel (Ni), % 0 to 0.3
17.5 to 19.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0.18 to 0.24
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0.1 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.010
Vanadium (V), % 0 to 0.1
0