EN 1.0571 Steel vs. SAE-AISI 4817 Steel

Both EN 1.0571 steel and SAE-AISI 4817 steel are iron alloys. They have a very high 96% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is SAE-AISI 4817 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 220
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
350
Tensile Strength: Ultimate (UTS), MPa 550
560
Tensile Strength: Yield (Proof), MPa 310
370

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
52
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
4.3
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.8
Embodied Energy, MJ/kg 21
24
Embodied Water, L/kg 49
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
370
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 17
17

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0.15 to 0.2
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 96.5 to 99
94.7 to 95.9
Manganese (Mn), % 0.9 to 1.7
0.4 to 0.6
Molybdenum (Mo), % 0 to 0.080
0.2 to 0.3
Nickel (Ni), % 0 to 0.3
3.3 to 3.8
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040
Vanadium (V), % 0 to 0.1
0