EN 1.0571 Steel vs. SAE-AISI 8620 Steel

Both EN 1.0571 steel and SAE-AISI 8620 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is SAE-AISI 8620 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
150 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
13 to 31
Fatigue Strength, MPa 220
270 to 360
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
340 to 420
Tensile Strength: Ultimate (UTS), MPa 550
520 to 690
Tensile Strength: Yield (Proof), MPa 310
360 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
20
Embodied Water, L/kg 49
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
86 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 260
340 to 880
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
18 to 24
Strength to Weight: Bending, points 19
18 to 22
Thermal Diffusivity, mm2/s 14
10
Thermal Shock Resistance, points 17
15 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0.18 to 0.23
Chromium (Cr), % 0 to 0.3
0.4 to 0.6
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 96.5 to 99
96.9 to 98
Manganese (Mn), % 0.9 to 1.7
0.7 to 0.9
Molybdenum (Mo), % 0 to 0.080
0.15 to 0.25
Nickel (Ni), % 0 to 0.3
0.4 to 0.7
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040
Vanadium (V), % 0 to 0.1
0