EN 1.0920 Steel vs. ACI-ASTM CF16Fa Steel

Both EN 1.0920 steel and ACI-ASTM CF16Fa steel are iron alloys. They have 69% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0920 steel and the bottom bar is ACI-ASTM CF16Fa steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
160
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
28
Fatigue Strength, MPa 270
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 380
230

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
980
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 50
16
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
17
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
3.3
Embodied Energy, MJ/kg 22
47
Embodied Water, L/kg 50
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 380
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 14
4.2
Thermal Shock Resistance, points 17
12

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.2
0 to 0.16
Chromium (Cr), % 0 to 0.3
18 to 21
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 96.1 to 99.08
62.1 to 72.4
Manganese (Mn), % 0.9 to 1.7
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
0.4 to 0.8
Nickel (Ni), % 0 to 0.5
9.0 to 12
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 2.0
Sulfur (S), % 0 to 0.030
0.2 to 0.4
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.12
0