EN 1.0920 Steel vs. EN 1.4869 Casting Alloy

EN 1.0920 steel belongs to the iron alloys classification, while EN 1.4869 casting alloy belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0920 steel and the bottom bar is EN 1.4869 casting alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 23
5.7
Fatigue Strength, MPa 270
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 380
310

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 400
1200
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 50
10
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
70
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 1.6
7.7
Embodied Energy, MJ/kg 22
110
Embodied Water, L/kg 50
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
26
Resilience: Unit (Modulus of Resilience), kJ/m3 380
230
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
17
Thermal Diffusivity, mm2/s 14
2.6
Thermal Shock Resistance, points 17
14

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.2
0.45 to 0.55
Chromium (Cr), % 0 to 0.3
24 to 26
Cobalt (Co), % 0
14 to 16
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 96.1 to 99.08
11.4 to 23.6
Manganese (Mn), % 0.9 to 1.7
0 to 1.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.5
33 to 37
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.015
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.5
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Tungsten (W), % 0
4.0 to 6.0
Vanadium (V), % 0 to 0.12
0